Investigation of tribological properties of CarbonX coating deposited on 100Cr6 steel

Abstract

The article deals with a reduction of friction coefficient of bearing steel 100Cr6. Reduction of friction was achieved by means of a CarbonX DLC coating. The coating exhibited excellent friction and mechanical properties. This coating was applied to samples made of 100Cr6 bearing steel. The friction results of the CarbonX coating were compared to the friction results of the 100Cr6 bearing steel. Reducing the friction of 100Cr6 bearing steel resulted in reduced wear and increase lifetime. The friction process of the samples will take place in an environment without lubrication. The aim of the article is to verify the behaviour of the DLC coating without the presence of lubricant in the friction node. The achieved results are to be interpreted in the conclusion of article.

Keywords

• tribology
• dlc coating
• 100cr6 steel
• friction