Use of Potabilized Water Sludge in the Production of Low-Energy Blended Calcium Sulfoaluminate Cements

Abstract

Ordinary Portland cement (OPC) manufacture determines about 8% of the global anthropogenic CO2 emissions. This has led to both the cement producers and the scientific community to develop new cementitious materials with a reduced carbon footprint. Calcium sulfoaluminate (CSA) cements are special hydraulic binders from non-Portland clinkers; they represent an important alternative to OPC due to their peculiar composition and significantly lower impact on the environment. CSA cements contain less limestone and require lower synthesis temperatures, which means a reduced kiln thermal energy demand and lower CO2 emissions. CSA cements can also be mixed with supplementary cementitious materials (SCMs) which further reduce the carbon footprint. This article was aimed at evaluating the possibility of using different amounts (20 and 35% by mass) of water potabilization sludges (WPSs) as SCM in CSA-blended cements. WPSs were treated thermally (TT) at 700° in order to obtain an industrial pozzolanic material. The hydration properties and the technical behavior of two different CSA-blended cements were investigated using differential thermal–thermogravimetric and X-ray diffraction analyses, mercury intrusion porosimetry, shrinkage/expansion and compressive strength measurements. The results showed that CSA binders containing 20% by mass of TTWPSs exhibited technological properties similar to those relating to plain CSA cement and were characterized by more pronounced eco-friendly features.

Keywords

• low-CO₂ binders
• calcium sulfoaluminate cements
• supplementary cementitious materials
• hydration
• expansion
• mechanical strength