Micro-Shear Bands and Their Enhancement on High Temperature Strength of Mg-Gd-Y-Zr Alloy

Abstract

When Mg-Gd-Y-Zr alloy is cold forged, a large number of nano-micro shear bands are formed inside the grains. It is observed that micro-shear bands hinder the sliding of dislocations, resulting in an increase in tensile strength at elevated temperatures. The subsequent aging treatment further strengthens the alloy. Compared with unforged aged alloys, aged samples with pre-generated micro-shear bands exhibit higher strength at room temperature to 250 °C, but exhibit similar properties at higher temperatures. Microstructure characterization and fracture behavior analysis indicate that the transformation of deformation mode from dislocation sliding to grain boundary activity is mainly due to the change of mechanical properties with temperature. In addition, the alloy precipitates with the aid of dislocations during tension, and exhibits higher strength at 200 °C than that at room temperature.

Keywords

• micro-shear bands
• strength
• Mg-Gd-Y-Zr alloy
• dislocation