Catalytic combustion of lean methane over different Co3O4 nanoparticle catalysts

Abstract

Three types of Co3O4 catalyst, namely Co3O4 nanoparticles (denoted as Co3O4-NPs, ∼12 nm in diameter), Co3O4 nanoparticles encapsulated in mesoporou s SiO2 (denoted as Co3O4@SiO2), and Co3O4 nanoparticles inside microporous SiO2 hollow sub-microspheres (denoted as Co3O4-in-SiO2), were explored to catalyze the combustion of lean methane. It was found that the methane conversion over the three catalysts has the order of Co3O4-NPs ≈ Co3O4@SiO2 > Co3O4-in-SiO2 due to the different catalyst structure. The comparison experiments at high temperatures indicate the Co3O4@SiO2 has a significantly improved anti-sintering performance. Combined with the TEM and BET measurements, the results prove that the presence of the mesoporous SiO2 layer can maintain the catalytical activity and significantly improve the anti-sintering performance of Co3O4@SiO2. In contrast, the microporous SiO2 layer reduces the catalytical activity of Co3O4-in-SiO2 possibly due to its less effective diffusion path of combustion product. Thus, the paper demonstrates the pore size of SiO2 layer and catalyst structure are both crucial for the catalytical activity and stability.

Keywords

• Co3O4 nanoparticles
• Catalytic combustion
• Methane
• Mesoporous SiO2
• Anti-sintering