International Journal of Engineering and Technology Innovation (Jul 2012)
Nano-mechanical Behaviour and Mmicrostructural Evolution of Cu/Si Thin Films at Different Annealing Temperatures
Abstract
This study investigates the nano-mechanical properties of as-deposited Cu/Si thin films indented to a depth of 2000 nm using a nanoindentation technique. Cu films with a thickness of 1800 nm are deposited on (100) silicon substrates and the indented specimens are then annealed at temperatures of 160℃ and 210℃, respectively, using rapid thermal annealing (RTA) technique. The results show that the hardness and Young’s modulus of the Cu/Si thin films have maximum values of 0.82 GPa and 95 GPa, respectively. The TEM observations show that the specimens annealed at a temperature of 160℃, the amorphous nature of the microstructure within the indented zone is maintained. However, annealed at a higher temperature of 210℃, the indentation affected zone consists of Copper silicide (η-Cu3Si) precipitates are observed in the annealed specimens. Overall, the results presented in this study confirm that the annealing temperature has a significant effect on the formation of η-Cu3Si in nanoindented Cu/Si thin-film systems.