Surfaces (Aug 2024)

Analysis, Assessment, and Mitigation of Stress Corrosion Cracking in Austenitic Stainless Steels in the Oil and Gas Sector: A Review

  • Mohammadtaghi Vakili,
  • Petr Koutník,
  • Jan Kohout,
  • Zahra Gholami

DOI
https://doi.org/10.3390/surfaces7030040
Journal volume & issue
Vol. 7, no. 3
pp. 589 – 642

Abstract

Read online

This comprehensive review examines the phenomena of stress corrosion cracking (SCC) and chloride-induced stress corrosion cracking (Cl-SCC) in materials commonly used in the oil and gas industry, with a focus on austenitic stainless steels. The study reveals that SCC initiation can occur at temperatures as low as 20 °C, while Cl-SCC propagation rates significantly increase above 60 °C, reaching up to 0.1 mm/day in environments with high chloride concentrations. Experimental methods such as Slow Strain Rate Tests (SSRTs), Small Punch Tests (SPTs), and Constant-Load Tests (CLTs) were employed to quantify the impacts of temperature, chloride concentration, and pH on SCC susceptibility. The results highlight the critical role of these factors in determining the susceptibility of materials to SCC. The review emphasizes the importance of implementing various mitigation strategies to prevent SCC, including the use of corrosion-resistant alloys, protective coatings, cathodic protection, and corrosion inhibitors. Additionally, regular monitoring using advanced sensor technologies capable of detecting early signs of SCC is crucial for preventing the onset of SCC. The study concludes with practical recommendations for enhancing infrastructure resilience through meticulous material selection, comprehensive environmental monitoring, and proactive maintenance strategies, aimed at safeguarding operational integrity and ensuring environmental compliance. The review underscores the significance of considering the interplay between mechanical stresses and corrosive environments in the selection and application of materials in the oil and gas industry. Low pH levels and high temperatures facilitate the rapid progression of SCC, with experimental results indicating that stainless steel forms passive films with more defects under these conditions, reducing corrosion resistance. This interplay highlights the need for a comprehensive understanding of the complex interactions between materials, environments, and mechanical stresses to ensure the long-term integrity of critical infrastructure.

Keywords