Formation of Hydrogels Based on a Copolymer of <i>N</i>-Vinyl-2-pyrrolidone and Glycidyl Methacrylate in the Presence of the Reaction Product of 1,3-Dimethylmidazolium Dimethylphosphate and Elemental Sulfur

Abstract

The aim of the study is to search for a reaction that provides the possibility of tandem “one-pot” formation of polymer networks during radical copolymerization of N-vinyl-2-pyrrolidone and glycidyl methacrylate. It was shown that the addition of recently synthesized 1,3-dimethylimidazolium (phosphonooxy-)oligosulfanide makes it possible to obtain a cross-linked copolymer in one stage as a result of radical copolymerization of N-vinyl-2-pyrrolidone and glycidyl methacrylate with a molar ratio of monomers less than 1.4. The structure of the copolymerization products of N-vinyl-2-pyrroldione and glycidyl methacrylate formed in the presence of 1,3-dimethylimidazolium (phosphonooxy-)oligosulfanide was characterized by 1H NMR, FTIR and MALDI spectroscopy. 1H NMR spectroscopy revealed an interaction under moderate heating between glycidyl methacrylate and 1,3-dimethylimidazolium (phosphonooxy-)oligosulfanide, accompanied by the formation of a mixture of unsaturated products of complex structure, presumably acting as crosslinking agents. It is shown that when the molar ratio of N-vinyl-2-pyrroldione/glycidyl methacrylate comonomers is 0.89, a densely crosslinked copolymer is formed, capable of limited swelling in water with a velocity constant of 5.06 × 10−2 min−1 and an equilibrium degree of swelling of about 227%.

Keywords

• PVP hydrogels
• “one-pot” synthesis
• swelling kinetics
• medical hydrogels
• <i>N</i>-vinyl-2-pyrrolidone
• glycidyl methacrylate