Effect Mechanism of Material Ratio on Ultrasonic P-wave Velocity in Coal Based Paste Fill Materials

Abstract

This research is designed to investigate the variations in ultrasonic p-wave velocity in various coal based paste fill materials used for recovering standing pillars in closed/closing coal mines, with consideration given to the effects of numerous material-related factors. For this purpose, orthogonal tests were designed. The evaluation was performed on the effects of four variables on the ultrasonic p-wave velocities in samples, using coal grains as the primary material. These variables consisted of the coal grains’ particle size (PA), high-water material content (PB), cement content (PC), and water content (PD). The experimental results show the following: (1) Ultrasonic p-wave velocity of coal based paste fill materials are measured within the range of 1.596 to 2.357 km/s, and these are classified (in descending order) as PD, PB, PC, and then PA, based on their effects on ultrasonic p-wave velocity. (2) Ultrasonic p-wave velocity is positively correlated with compressive strength and shear strength; the correlation coefficients are 0.82 and 0.69, respectively. (3) Changes in the ultrasonic p-wave velocity of coal based paste fill materials, when exposed to various factors, have been characterized by fitted formulae. It was observed that the velocity maintained a quadratic polynomial correlation with factor PB and exponential correlations with factors PA, PC, and PD. The comprehensive predictive model, reflecting the characteristics of the ultrasonic p-wave velocity in response to the combined influence of these four factors, was developed through the utilization of fitted equations pertaining to individual factor variations. Subsequently, this model underwent verification.

Keywords

• coal based
• paste fill material
• correlation coefficient
• ultrasonic wave speed
• formula fitting