Structure and electrical properties of Eu-doped SrBi2Nb2O9 ceramics

Abstract

Structure and dielectric properties of Eu-doped SrBi2Nb2O9 ceramics (with 0, 20 and 35 at.% of Eu), prepared by the solid-state method and sintering, were investigated. XRD, FTIR and SEM measurements were provided to validate the characteristic structural features of the obtained ceramics. For all samples, the orthorhombic structure was identified through XRD analysis. SEM results confirmed that the fabricated samples have relatively dense structure with rod- and plate-like grains typical for Aurivillius layered structures. Dielectric results showed that the doping with Eu decreases dielectric constant and reduces dielectric loss. Movement of the dielectric peak towards higher temperatures appearing at about 400 °C with increase of frequency indicates on relaxor behaviour of the sample with 35 at.% of Eu.

Keywords

• SrBi2Nb2O9
• ceramics
• microstructure
• dielectric