Influence of Austenitisation Temperature and Time on Martensitic and Isothermal Bainite Phase Transformation of Spring Steel

Abstract

The influence of austenitisation temperature and time on the martensitic and isothermal bainite transformation of 51CrV4 spring steel was analysed. Based on the analysis of dilatometric curves, the martensite start temperatures (MS) were determined at different austenitisation temperatures (800–960 °C) and austenitisation times (5–30 min). At a temperature of 800 °C, a partial austenitic transformation occurred, and undissolved chromium carbides were present in the matrix. At higher temperatures, the austenitic transformation was complete, and the temperature MS increased with the austenitisation temperature. The temperature of the isothermal phase transformation has a stronger effect on the bainite transformation, which has different effects on the stability of the austenite and the diffusion processes. The microstructure of isothermal bainite transformation samples at 330, 430 and 520 °C was characterised by optical microscopy and dilatometric curves. Lower bainite was formed at a bainitic transformation temperature of 330 °C, and a combination of upper and lower bainite was characterised at a transformation temperature of 430 °C. In the samples transformed at 520 °C, a smaller proportion of lower bainite formed in addition to the upper bainite and martensite. Some allotriomorphic ferrite formed along the boundaries of the austenitic grains.

Keywords

• spring steel
• 51CrV4
• dilatometry
• martensitic transformation
• bainite transformation