Electromagnetic Wave-Absorbing and Bending Properties of Three-Dimensional Honeycomb Woven Composites

Abstract

To avoid the delamination of the traditional three-dimensional (3-D) honeycomb electromagnetic (EM) absorbing composites and improving the defects of low mechanical properties, the 3-D honeycomb woven fabrics were woven on the ordinary loom by practical design. The fabrication of 3-D honeycomb woven EM absorbing composites was based on carbon black/carbonyl iron powder/basalt fiber/carbon fiber/epoxy resin (CB/CIP/BF/CF/EP) by the vacuum-assisted resin transfer molding (VARTM) process. A CB/CIP composite absorbent study showed that CB/CIP composite absorbent belongs to a magnetic loss type absorbent. Adding CB/CIP significantly improved the absorption performance of composite, increased the absorption peak and the effective absorption bandwidth (EAB), but the bending performance decreased. The normalization analysis results showed that when the thickness was 15 mm, the mechanical properties and EM wave-absorbing properties of the 3-D honeycomb woven composite were the best matches. The morphological characteristics and displacement load curves of the composite after fracture were analyzed. The bending failure modes were brittle fracture of the fiber bundle, matrix cracking, and typical shear failure. Despite the above failure mechanism, the 3-D honeycomb woven EM absorbing composites still has good integrity without delamination.

Keywords

• 3-D honeycomb woven fabric
• CB/CIP
• mechanical property
• EM wave-absorbing property