Investigation of alkali-silica reaction on mortars with alternative binder systems: Alkali activated Slags and Celitement

Julia T. Sonntag; Ravi A. Patel; David Alós Shepherd; Frank Dehn

Cement (Sep 2023)

Investigation of alkali-silica reaction on mortars with alternative binder systems: Alkali activated Slags and Celitement

Julia T. Sonntag,
Ravi A. Patel,
David Alós Shepherd,
Frank Dehn

Affiliations

Julia T. Sonntag: Karlsruhe Institute of Technology (KIT), Institute of Building Materials and Concrete Structures (IMB), DE-76131 Karlsruhe, Germany; Materials Testing and Research Institute Karlsruhe (MPA), Karlsruhe Institute of Technology (KIT), DE-76131 Karlsruhe, Germany
Ravi A. Patel: Karlsruhe Institute of Technology (KIT), Institute of Building Materials and Concrete Structures (IMB), DE-76131 Karlsruhe, Germany; Materials Testing and Research Institute Karlsruhe (MPA), Karlsruhe Institute of Technology (KIT), DE-76131 Karlsruhe, Germany; Corresponding author at: Karlsruhe Institute of Technology (KIT), Institute of Building Materials and Concrete Structures (IMB), DE-76131 Karlsruhe, Germany.
David Alós Shepherd: Karlsruhe Institute of Technology (KIT), Institute of Building Materials and Concrete Structures (IMB), DE-76131 Karlsruhe, Germany; Materials Testing and Research Institute Karlsruhe (MPA), Karlsruhe Institute of Technology (KIT), DE-76131 Karlsruhe, Germany
Frank Dehn: Karlsruhe Institute of Technology (KIT), Institute of Building Materials and Concrete Structures (IMB), DE-76131 Karlsruhe, Germany; Materials Testing and Research Institute Karlsruhe (MPA), Karlsruhe Institute of Technology (KIT), DE-76131 Karlsruhe, Germany

Journal volume & issue: Vol. 13
p. 100078

Abstract

Read online

This study investigates the resistance against alkali-silica reaction (ASR) of two alternative binder systems, alkali-activated slag (AAS) and Celitement (Celite). Experimental studies on expansion and mechanical strength are carried out. Coupled kinetic and equilibrium thermodynamic modeling is used to clarify the role of binder chemistry on ASR. It was observed that under accelerated conditions OPC based mortars were more susceptible to ASR compared to AAS and Celite-based mortars. Based on experimental and modeling results, a correlation is shown between the dissolution of silica and the degree of expansion, but no correlation was found between the predicted amount of ASR products and the measured degree of expansion. Finally, the expansion degree could only be correlated with the reduction in compressive and flexural tensile strength for ASR-exposed samples.

Published in Cement

ISSN: 2666-5492 (Online)
Publisher: Elsevier
Country of publisher: Netherlands
LCC subjects: Technology: Chemical technology: Cement industries
Website: https://www.journals.elsevier.com/cement

About the journal

Abstract

Keywords