Room temperature formation of Hf-silicate layer by pulsed laser deposition with Hf-Si-O ternary reaction control

Abstract

We investigated the room temperature growth of HfO2 layers on Si substrates by pulsed laser deposition under ultra-high vacuum conditions. The laser fluence (LF) during HfO2 layer growth was varied as a growth parameter in the experiments. X-ray photoemission spectroscopy (XPS) was used to observe the interface chemical states of the HfO2/Si samples produced by various LFs. The XPS results indicated that an interface Hf-silicate layer formed, even at room temperature, and that the thickness of this layer increased with increasing pulsed LF. Additionally, Hf-Si bonds were increasingly formed at the interface when the LF was more than 2 J/cm2. This bond formation process was related to decomposition of HfO2 to its atomic states of Hf and O by multiphoton photochemical processes for bandgap excitation of the HfO2 polycrystalline target. However, the Hf-Si bond content of the interface Hf-silicate layer is controllable under high LF conditions. The results presented here represent a practical contribution to the development of room temperature processing of Hf-compound based devices.