Archives of Metallurgy and Materials (Mar 2017)

Impact of electro slag remelting on 14 109 steel properties

  • Pribulová A.,
  • Futáš P.,
  • Kmita A.,
  • Márasová D.,
  • Holtzer M.

DOI
https://doi.org/10.1515/amm-2017-0025
Journal volume & issue
Vol. 62, no. 1
pp. 181 – 185

Abstract

Read online

The Electro Slag Remelting (ESR) is one of the remelting processes in the field of metal refinery. In this process, the slag plays various roles, such as heat generation, protection of melt, and chemical refining. The main objective of the experiments described in this article was to identify the most appropriate slag composition for the electro slag remelting of the steel in order to achieve the chemical composition compliant with the standard applicable to the given steel, minimum sulphur content, minimum contents of oxide and sulphide inclusions, as well as mechanical properties corresponding to the standard applicable to the steel STN 14 109. Ten electrodes were remelted, whereas the remelting was carried out under 8 slags. The used slags containing 70% of CaF2 and 30% of Al2O3 with different addition of CaO, the slags consisted of the same components as previous slags, whereas the ratio of individual components was 1:1:1, and with SiO2 and MgO and slag without Al2O3. With regard to all the above mentioned facts, the slag types which may be regarded as the most appropriate for the STN 14 109 steel remelting are the basic slags containing 70% of CaF2 - 30% of Al2O3 with added 30 and 45 weight % of CaO.

Keywords