Boletín de la Sociedad Española de Cerámica y Vidrio (Feb 2011)
Influencia de las condiciones de procesamiento sobre las propiedades dieléctricas y microestructurales de cerámicos de K<sub>1/2</sub>Na<sub>1/2</sub>NbO<sub>3</sub>
Abstract
The objective of this work was to analyze different processing condition of Na1/2K1/2NbO3 (KNN) in order to obtain a material with good properties and without secondary phases. Solid state reaction method was used and the influence of milling time, calcination temperature and time, and sintering temperature was analyzed. It was found that sintering temperatures were limited by the component decomposition. Also, it was observed that samples sintered at 1125 ºC showed the highest density and permittivity with a homogeneous structure. In general, samples calcined at higher temperatures and times showed the best properties.El objetivo de este trabajo es analizar diferentes condiciones de procesamiento del K1/2Na1/2NbO3 (KNN) que permitan obtener un material con buenas propiedades y libre de fases secundarias. Se implementó el método de activación mecanoquímica de los precursores y posterior reacción en estado sólido. Se analizaron las principales condiciones de procesamiento (tiempo de molienda, temperaturas de calcinación y sinterizado), y se determinaron las propiedades dieléctricas y microestructurales de cada sistema. Se encontró que las temperaturas máximas de calcinación estuvieron limitadas por la descomposición de los constituyentes. También se observó que las pastillas sinterizadas a 1125ºC registraron mayor densidad, mayor permitividad y una microestructura homogénea. En general, se observó que los sistemas calcinados a mayores temperaturas y por tiempos mayores tuvieron mejores propiedades.
Keywords