Enhanced Grain Refinement and Precipitation of the IEECAPed Mg-Sm-Zn-Zr Alloy by Nd Addition

Abstract

Achieving magnesium-rare earth alloys with excellent mechanical properties remains a challenging goal in the aerospace industry. The integrated extrusion and equal channel angular pressing were employed to refine grain and improve the mechanical properties of Mg-xNd-2.0Sm-0.4Zn-0.4Zr alloys. The effect of Nd element on microstructure and mechanical properties of the extruded and subsequently aged alloys were carried out by varying the amount of the Nd element from 0 wt.% to 2.5 wt.%. The optical microscopy results indicated that the grain size was remarkably refined by the addition of Nd element. The grain size decreased from 29.7 μm to 10.9 μm with increasing of the Nd element from 0 wt.% to 2.5 wt.%. The transmission electron microscopy results showed that the nano-scaled basal lamellar precipitates, prismatic lamellar precipitates and granular precipitates were formed in α-Mg matrix. The amount of the precipitates increased significantly by the addition of Nd. Moreover, the strength of the alloys significantly improved with Nd. Superior strength and considerable plasticity were obtained as the content of Nd element reached 2.0 wt.%, while the tensile strength of the Mg-2.0Nd-Sm-Zn-Zr alloy (315 ± 5 MPa) increased by 35.8% with respect to the Nd-free alloy (232 ± 3 MPa).

Keywords

• Mg-rare earth alloy
• IEECAP
• microstructure
• mechanical properties