Impact of thermal oxidation parameters on micro-hardness and hot corrosion of Ti-6Al-3Mo-2Nb-2Sn-2Zr-1.5Cr alloy

Abstract

Abstract Protective oxide layers on Ti-6Al-3Mo-2Nb-2Sn-2Zr-1.5Cr (TC21) alloy with equiaxed microstructure considerably influence micro-hardness and hot corrosion resistance. The present work’s thermal oxidation of TC21 alloy was performed at 600, 700, and 800 °C for 5, 20, and 50 h durations. Hot corrosion methods in NaCl and NaCl + Na2SO4 salt media were applied to raw (unoxidized) and oxidized samples at 600 and 800 °C for 50 h. Hot corrosion was conducted at 600 °C for 5 cycles with 10-h steps. The best oxide layer thickness was observed at 800 °C, which increased with increased oxidation time and temperature. The surface hardness of the oxide layer at 800 °C was 900 ± 60 HV0.05 owing to the formation of TiO2 and Al2O3 phases. Raw material hardness was 342 ± 20 HV0.05, increasing threefold due to thermal oxidation. In the case of NaCl, weight loss dominated all samples except at 800 °C for 5 h. In the case of NaCl + Na2SO4, weight gain occurred at 600 and 800 °C for 5 h. Weight loss occurred for the raw samples and those processed at 800 °C for 20 and 50 h, where the oxide layer flaked off. Surface hardness increased upon hot corrosion testing because of the formation of brittle phases, such as TiO2 and Na4Ti5O12. Samples that oxidized at 800 °C for 5 h had the highest hardness and corrosion resistance.