Cr/13X Zeolite and Zn/13X Zeolite Nanocatalysts Used in Pyrolysis of Pretreated Residual Biomass to Produce Bio-Oil with Improved Quality

Abstract

By loading Cr and Zn on 13X zeolite, efficient nanocatalysts were prepared; they were characterized by different techniques and used for corn cobs pyrolysis to produce bio-oil. The corn cobs biomass (CCB) was washed with sulfuric acid 0.1 M, and the characteristics of the pretreated biomass (PTCCB) were analyzed. Pyrolysis was performed at different catalyst-to-biomass ratios (C/B), and the composition of the obtained bio-oil was determined. The results showed that the crystallinity of the nanocatalysts was slightly lower than that of the pattern 13X zeolite. The surface observation of the nanocatalysts showed the presence of pores and particles, which are quite evenly dispersed on the surface, and no difference was observed in the morphology of the Zn/13X zeolite and Cr /13X zeolite nanocatalysts. In comparison to 13X zeolite, the morphological changes, metal dispersion, and surface area decrease of both Zn/13X and Cr/13X zeolite nanocatalysts could be observed. Pyrolysis tests demonstrated that the use of Zn/13X zeolite and Cr/13X zeolite nanocatalysts could be very profitable to obtain a high conversion to hydrocarbons of the compounds containing oxygen, and consequently, the quality of the bio-oil was improved.

Keywords

• nanocatalysts
• 13X zeolite support
• corn cobs biomass
• acid washing
• pyrolysis
• bio-oil