Influence of Nanoclay on the Thermo-Mechanical Properties of Silicone Pressure-Sensitive Adhesives

Abstract

This research was carried on newly obtained innovative materials—self-adhesive one-sided tapes based on silicone pressure-sensitive adhesives. In order to obtain tapes, the stable adhesive composition was subjected to physical modification by incorporating into it various amounts of selected silicon fillers. The produced pressure-sensitive adhesives were tested for viscosity and thermogravimetric analysis, as well as the manufactured tapes; i.e., peel adhesion, tack, cohesion at room and elevated temperature, SAFT test (shear adhesive failure temperature), and shrinkage. The prepared self-adhesive tapes retained their self-adhesive properties at a level close to the initial level while increasing the thermal resistance by 70–75 °C, reaching the level of 220–225 °C. The new self-adhesive materials have application potential and can be used as a material for special applications in the field of electrical engineering and heavy industry.

Keywords

• pressure-sensitive adhesives
• thermal crosslinking
• silicone additives
• dellite