Study on the Growth Mechanism of K2Ti4O9 Crystal

Abstract

Potassium hexatitanate (K2Ti4O9) whiskers were prepared by the kneading–drying–calcination method. After the preparation of products under different calcination temperatures and holding times, their morphology and structure were characterized by thermogravimetric and differential thermal, X-ray diffraction (XRD), scanning electron microscopy and transmission electron microscopy. The XRD analysis showed that the reaction mixture was completely converted to K2Ti4O9 crystals at 800 °C when the T/K ratio was 3. Based on the analysis of LS (liquid–solid) growth mechanism, the corresponding transformation reaction mechanism during the roasting was elucidated. K2Ti4O9 whiskers grow mainly through the parallel action at a low temperature. With the increase in temperature, the series effect is obvious.