Production and Characterization of Nanostructured Powders of Nd₂Fe₁₄B and Fe₉₀Al₁₀ by Mechanical Alloying

Abstract

The objective of this work is to evaluate the applicability of exchange coupling between nanoparticles of Nd2Fe14B (hard magnetic material) and Fe90Al10 (soft magnetic material), as permanent magnets produced by surfactant-assisted mechanical alloying. The obtained powders were then mixed with 85% of the Nd2Fe14B system and 15% of the Fe90Al10 system and subsequently sintered at 300 °C, 400 °C and 500 °C for one hour. The results obtained by Mössbauer spectrometry (MS) show a ferromagnetic behavior with six magnetic sites represented by sextets (16k1, 16k2, 8j1, 8j2, 4c and 4e), characteristic of the Nd2Fe14B system. X-ray diffraction (XRD) results show a tetragonal and BCC structure for the Nd2Fe14B and FeAl systems, respectively. The results obtained by vibrating sample magnetometry (VSM), for mixtures of the Nd2Fe14B and Fe90Al10 sy stems sintered at 300 °C, 400 °C and 500 °C, allow for the conclusion that the coercive field (Hc) decreases drastically with temperature and the percentage of soft phase at values of Hc = 132 Oe compared to the coercive field values reported for Nd2Fe14B Hc = 6883 Oe, respectively. Images obtained by transmission electron microscopy (TEM), for the Fe90Al10 system, show a tendency for the nanoparticles to agglomerate.

Keywords

• magnetic materials
• Mössbauer spectrometry
• mechanical alloying
• nanoparticle