H₂-Based Processes for Fe and Al Recovery from Bauxite Residue (Red Mud): Comparing the Options

Abstract

To tackle the challenge of bauxite residue (BR), generated during the alumina production, as well as to recover some of its metal content, three combinatory H2-based processes were utilized. Firstly, Greek BR was mixed with NaOH to produce water soluble Na-aluminates and was roasted under pure H2 gas in order to reduce the Fe+3 content. Then the first process combined water leaching and magnetic separation, the second water leaching and melting and the last included wet magnetic separation. The water media resulted in the dissolution of Na-aluminate phases and the production of Al, Na-ion rich leachates. From these, pregnant leaching solutions recovery of Al was 78%, 84% and for the third case it reached 91%. Concerning Na recovery, it could reach 94%. Both melting process and magnetic separation aimed for Fe recovery from the material. The former case however still needs to be optimized, here its concept is introduced. The magnetic fraction, after the dry magnetic separation, varied in Fe content from 31.57 wt.% to 38.50 wt.%, while after the wet magnetic separation it reached 31.85 wt.%.

Keywords

• H₂ reduction
• bauxite residue
• red mud
• Al recovery
• Fe recovery