Comparative evaluation of antibacterial and anti-adherent properties between titanium oxide, silver dioxide-coated, and conventional orthodontic wires against Streptococcus Sanguis causing gingivitis

Abstract

Objective: To compare the antibacterial and anti-adherent properties of conventional stainless steel (SS) orthodontic wires and surface-modified silver dioxide-coated and titanium oxide-coated SS orthodontic wires against Streptococcus sanguis causing gingivitis. Materials and Methods: The study used 60 orthodontic SS wire specimens, organized into six groups of ten each. The control group had uncoated wires, and the experimental group featured wires coated with silver dioxide and titanium oxide. Surface modification was done using DC sputtering, and microbiological tests assessed the antibacterial and anti-adherent properties of the AgO2- and TiO2-coated wires. Results: This study demonstrated the antibacterial effect against S. sanguis in orthodontic wires coated with the photocatalytic AgO2 and TiO2 compared to the uncoated wires. Also, this study demonstrated an anti-adherent effect in the AgO2- and TiO2-coated orthodontic wires. Moreover, the bacterial accumulation on orthodontic wires coated with AgO2 and TiO2 was lower compared to that on the uncoated wires. Conclusion: During orthodontic treatment, the formation of dental plaque can be prevented by coating the surface of stainless-steel orthodontic wires with photocatalytic AgO2 and TiO2. Compared to silver dioxide, the titanium oxide-coated SS orthodontic wires showed better antibacterial and anti-adherent properties.

Keywords

• anti-bacterial
• anti-adhesion
• gingivitis
• orthodontic wire
• photo-catalytic
• silver dioxide
• streptococcus sanguis
• titanium oxide