Conceptual Design of a Pilot Process for Manufacturing Aluminum-Based Intermetallic Compound Powders

Abstract

The FeAl intermetallic compound is of great interest for industry due to its low density, low cost and high mechanical and corrosion resistance, so it can replace stainless steels and nickel-based alloys for some applications. In previous publications, the concept (principle) test for a novel FeAl powder manufacturing process has been shown. It consists mainly of the following stages: (a) metallic strip manufacture through rapid solidification, (b) water vapor exposure of these metallic strips for their disintegration and powder generation and (c) powder drying. Experimental tests were performed for 2 g of the FeAl intermetallic compound. However, this process can be extended to manufacture any other intermetallic compound containing aluminum, such as TiAl, NiAl, CoAl or any other that can be obtained from every element that can combine with aluminum, if the aluminum content is between 55 and 60 at.%. Nowadays, this process is at technology readiness level (TRL) 3. Therefore, in this paper, a process equipment up-scaling configuration for producing up to 15 kg powder is proposed. This manufacturing process is an industrial alternative to those commonly used to produce powders of this type of intermetallic compounds, such as mechanical alloying (MA). Moreover, several alternatives for employing renewable energy sources are given, making it even more environmentally sustainable.

Keywords

• intermetallic compound
• FeAl
• rapid solidification
• up-scaling
• solar energy