Characterization of Ca Precipitation in Al-Mg Alloys Containing a Trace of Ca During Homogenization

Abstract

In this study, precipitation of Ca in Al-Mg alloys containing a trace of Ca during homogenization was investigated using a transmission electron microscope (TEM) and calculated phase diagrams. TEM result indicated that the Ca-based particles found in the examined sample are Ca7Mg7.5Si14. From the calculation of Scheil-Gulliver cooling, it was found that the Ca was formed as Al4Ca and C36 laves phases with Mg2Si and Al13Fe4 from other impurities phase during solidification. No Ca-Mg-Si ternary phase existed at the homogenization temperature in the calculated phase diagram. From the phase diagram of Al-Al4Ca-Mg2Si three-phase isothermal at 490℃, it was shown that Ca7Mg6Si14 phase co-exists with Al, Mg2Si and Al4Ca in the largest region and with only Al and Mg2Si in Al4Ca-poor regions. It was thought that the Ca7Mg6Si14 ternary phase was formed by the interaction between Mg2Si and Al4Ca considering that the segregation can occur throughout the entire microstructures.

Keywords

• al-mg system
• precipitation
• mg+al2ca mater alloy
• transmission electron microscope
• phase diagram