Physical simulation of finish rolling of microalloyed steels in isothermal conditions

Abstract

The aim of this work was to establish a temperature of finish rolling stage of Nb/Ti microalloyed steel containing 0.06 wt.% C, 0.77 wt.% Mn, 0.039 wt.% Nb and 0.015 wt.% Ti, using physical simulation. Samples were subjected to laboratory simulation at a twist plastometer at high temperatures, i.e. between 825 and 950°C. Five pass deformation and interpass times were selected in accordance with a processing parameters at five stand finishing hot strip mill. Restoration (recovery and/or recrystallization) behavior was evaluated by calculation of Fraction Softening (FS) and Area Softening Parameter (ASP) values. At 950°C all individual pass stress-strain curves, FS and ASP show full recrystallization in all interpass intervals. On the other hand, with a decrease in temperature to the interval of 875-825°C, the extent of restoration is decreasing, leading to recovery as a sole softening mechanism at 825°C, which was confirmed by the stress-strain curve shape, and values of FS and ASP. It is assumed that, due to high supersaturation, strain-induced precipitation promoted pinning of grain and subgrain boundaries and suppressed recrystallization. Therefore, the critical temperature for finish rolling was estimated to be 825°C.

Keywords

• fraction softening
• mechanical metallography
• deformation
• recrystallization
• critical rolling temperatures
• controlled rolling