Xylan derived carbon sphere/graphene composite film with low resistance for supercapacitor electrode

Abstract

Abstract Reduced graphene oxide (rGO) films suffer from low capacitance for inner unreduced oxygen functional groups, restacking of sheets and high contact resistance. Herein, carbon spheres derived from renewable xylan were added to graphene oxide with large sheet area to fabricate film by gelation and filtration, followed by in situ reduction for high-performance flexible supercapacitor. rGO film with transverse size about 13 μm showed a good specific capacitance of 967 mF/cm2 at a scanning rate of 5 mV/s and increased to 1786 mF/cm2 by in situ reducing its inner part, which generally remained oxidized due to outer hindering from hydrophobic graphene. Then, by hydrothermal carbonization of xylan and activation with KOH, activated carbon sphere (aXCS) was prepared, which had a diameter of 150–200 nm and a specific capacitance of 270 F/g. The aXCS acted as spacer and connector to avoid restacking of graphene sheets and decrease interlayer contact resistance, resulting 94% increase in capacitance performance from rGO film to aXCS/rGO film. Therefore, combined in situ reduction and enhancement through compositing aXCS, the final film (aXCS/rGO-AA) showed a boosted specific capacitance of 755 mF/cm2 at 1 mA/cm2 in double electrode system, power density of 22.5–2250 mW/cm2, and energy density of 11.88–25.2 mWh/cm2. Meanwhile, aXCS/rGO-AA had outstanding cycling stability that its specific capacitance maintained 108.7% after 10,000 cycles of charge–discharge, showing promising potential in wearable and portable electronics. Graphical abstract

Keywords

• Xylan
• Carbon sphere
• Graphene film
• In situ reduction
• Supercapacitor