Effects of High-Temperature Annealing Atmosphere on the Secondary Recrystallization Behavior and Magnetic Properties of Fe-3.2%Si-0.055%Nb Grain-Oriented Silicon Steel

Abstract

High-temperature annealing is a key step for the secondary recrystallization of grain-oriented silicon steel, which has an important effect on the final sharp Goss texture. In this work, the effects of three different annealing atmospheres during high-temperature annealing (100%H2, 25%N2 + 75%H2 and 50%N2 + 50%H2) on the secondary recrystallization microstructure and texture of Fe-3.2%Si-0.055%Nb low temperature grain-oriented silicon steel were analyzed by optical microscopy (OM) and electron back-scattered diffraction (EBSD) techniques, and the magnetic properties of the samples were compared. The results show that when the high-temperature annealing atmosphere is 100%H2, the texture of the grains with secondary recrystallization is mainly //ND orientation, but the grains without secondary recrystallization have a disordered orientation. When the high-temperature annealing atmosphere is 50%H2 + 50%N2, the secondary recrystallization grains present a Goss texture and brass texture. After high-temperature annealing in the 25%N2 + 75%H2 atmosphere, the sample can be fully recrystallized to obtain secondary recrystallization grains; the grain size is relatively uniform and the texture is mainly a Goss texture with a sharp edge. The content of this reaches 93.1%, the magnetic induction B800 is the highest, reaching 1.89 T, and the iron loss P1.7/50 is the lowest, reaching 1.33 W/kg.

Keywords

• 0.055% Nb grain-oriented silicon steel
• annealing atmosphere
• secondary recrystallization
• texture
• magnetic property