Effect of Ni element on microstructure and properties of cold-rolled 316 L austenitic stainless steel

Abstract

In this current investigation, the impact of Nickel (Ni) on the microstructural attributes and properties of a cold-rolled 316 L sheet was examined. The microstructure and phase configuration of austenitic stainless steels, specifically 316 L and 316LNi, were meticulously characterized through the utilization of metallography, X-ray Diffraction (XRD), and Electron Backscatter Diffraction (EBSD) techniques. Subsequent assessments were conducted to evaluate magnetic characteristics, microhardness, and tensile properties. The phase structure of both austenitic stainless steels conforms to a Face-Centered Cubic (FCC) crystal lattice, whereby the grain content oriented along the (110) plane progressively escalates with augmenting degrees of cold rolling. The magnetic conductivity of these austenitic stainless steels satisfactorily adheres to established standards. The incorporation of Nickel (Ni) into the alloy composition enhances the cold deformation capacity of 316 L stainless steel. However, substantial plastic deformation yields heightened dislocation density, thereby promoting enlarged grain dimensions upon solution treatment. Throughout subsequent cold rolling deformation sequences, the augmented grain size observed in 316LNi stainless steel leads to a reduction in dislocation density within the equivalently ordered cold-rolled plate. Simultaneously, this augmented grain size engenders a decline in grain boundary content coupled with an augmentation in twin content. Consequently, the interplay of grain coarsening, diminished dislocation density, and twin-induced softening collectively bestows upon 316LNi stainless steel a lower tensile strength compared to 316 L stainless steel, albeit accompanied by heightened plasticity.

Keywords

• 316 L austenitic stainless steel
• Ni element
• cold rolling
• magnetic conductivity
• strength-plasticity