Archives of Foundry Engineering (Jun 2024)

Microstructure and Mechanical Properties of the EN AC-AlSi12CuNiMg Alloy and AlSi Composite Reinforced with SiC Particles

  • G.G. Sirata,
  • K. Wacławiak,
  • A.J. Dolata

DOI
https://doi.org/10.24425/afe.2024.149271
Journal volume & issue
Vol. vol. 24, no. No 2
pp. 50 – 59

Abstract

Read online

There is growing interest in developing more advanced materials, as conventional materials are unable to meet the demands of the automotive, aerospace, and military industries. To meet the needs of these sectors, the use of advanced materials with superior properties, such as metal matrix composites, is essential. This paper discusses the evaluation of microstructural and mechanical properties of conventional eutectic EN AC-AlSi12CuNiMg aluminum alloy (AlSi12) and advanced composite based on EN AC-AlSi12CuNiMg alloy matrix with 10 wt% SiC particle reinforcement (AlSi12/10SiCp). The microstructure of these materials was investigated with the help of metallographic techniques, specifically using a light microscope (LM) and a scanning electron microscope (SEM). The results of the microstructural analysis show that the SiC particles are uniformly distributed in the matrix. The results of the mechanical tests indicate that the tensile properties and hardness of the AlSi12/10SiCp composite are significantly higher than those of the unreinforced eutectic alloy. For AlSi12/10SiCp composite, the tensile strength is 21% higher, the yield strength is 16% higher, the modulus of elasticity is 20% higher, and the hardness is 11% higher than unreinforced matrix alloy. However, the unreinforced AlSi12 alloy has a percentage elongation that is 16% higher than the composite material. This shows that the AlSi12/10SiCp composite has a lower ductility than the unreinforced AlSi12 alloy. The tensile specimens of the tested composite broke apart in a brittle manner with no discernible neck development, in contrast to the matrix specimens, which broke apart in a ductile manner with very little discernible neck formation.

Keywords