Fatigue and Fracture Properties of Laminated Bamboo Strips from Gigantochloa scortechinii Polyester Composites

Abstract

The fatigue and fracture properties of bamboo fiber composites made of woven layers were investigated. This study utilized a specific type of bamboo species named Gigantochloa scortechinii (Buluh Semantan). In these experiments, unsaturated polyester (UP) and bamboo fiber (BF) strips were prepared through a hand lay-up technique using 3-mm thick aluminum mould. The composite bamboo strips had a thickness of 1.5 mm. The strips were woven together to make a single layer. The layer was then laminated into several thicknesses. The specimens were then characterized using fatigue and fracture tests. A fatigue limit of 30 MPa and fracture toughness of 5 to 8 MPa √m were obtained. These findings suggest that the bamboo strips, based on unsaturated polyester, provided relatively good fatigue and fracture properties and a good method of reinforcing fibers to combat fatigue and fracture failures.

Keywords

• Bamboo strip
• Unsaturated polyester
• Gigantochloa scortechinii
• Mechanical testing
• Fatigue and fracture laminated composites