Co-Promoted Ni Nanocatalysts Derived from NiCoAl-LDHs for Low Temperature CO₂ Methanation

Abstract

Ni-based catalysts are prone to agglomeration and carbon deposition at high temperatures. Therefore, the development of Ni-based catalysts with high activities at low temperatures is a very urgent and challenging research topic. Herein, Ni-based nanocatalysts containing Co promoter with mosaic structure were prepared by reduction of NiCoAl-LDHs, and used for CO2 methanation. When the reaction temperature is 250 °C (0.1 MPa, GHSV = 30,000 mL·g−1·h−1), the conversion of CO2 on the NiCo0.5Al-R catalyst reaches 81%. However, under the same test conditions, the conversion of CO2 on the NiAl-R catalyst is only 26%. The low-temperature activity is significantly improved due to Co which can effectively control the size of the Ni particles, so that the catalyst contains more active sites. The CO2-TPD results show that the Co can also regulate the number of moderately basic sites in the catalyst, which is beneficial to increase the amount of CO2 adsorbed. More importantly, the NiCo0.5Al-R catalyst still maintains high catalytic performance after 92 h of continuous reaction. This is due to the confinement effect of the AlOx substrate inhibiting the agglomeration of Ni nanoparticles. The Ni-based catalysts with high performance at low temperature and high stability prepared by the method used have broad industrial application prospects.

Keywords

• CO₂ methanation
• low temperature
• Co additive
• NiCoAl-LDHs