Polyphenylene Sulfide Ultrafine Viscous Fibrous Membrane Modified by ZIF-8 for Highly Effective Oil/Water Separation under High Salt or Alkaline Conditions

Abstract

The oil/water separation in harsh environments has always been a challenging topic all over the world. In this study, the ZIF-8/PPS fiber membranes were fabricated via the combination of hot pressing and in situ growth. The distribution of ZIF-8 in the membranes was adjusted by changing the ZIF-8 in situ growth time, which could control the oil/water separation effect. Due to the hydrophilic nature of the ZIF-8/PPS fiber membranes, the water molecules in the oil-in-water emulsion could quickly penetrate into the fiber membrane under the drive of pressure, gravity, and capillary force, forming a water layer on the surface of the fiber membranes. The coupling of the water layer and the fiber structure prevented direct contact between the oil molecules and the fiber membrane, thereby realizing the separation of the emulsion. The results show that when the ZIF-8 in situ growth time was 10 h, the contact angle, the porosity, and the pure water flux of the ZIF-8/PPS fiber membranes were 72.5°, 52.3%, and 12,351 L/h·m2, respectively. More importantly, the separation efficiency of M10 was 97%, and the oil/water separation efficiency reached 95% after 14 cycles. This study provides a novel strategy for preparing MOFs/fiber materials for oil/water separation in harsh environments.

Keywords

• polyphenylene sulfide
• ZIF-8
• oil/water separation
• membrane
• chemical resistance