Laser powder bed fusion of diamond/N6 MMCs enabled by Ni-Ti coated diamond particles

Sheng Zhang; Minglu Ding; Lu Wang; Wenjun Ge; Wentao Yan

Materials & Design (May 2022)

Laser powder bed fusion of diamond/N6 MMCs enabled by Ni-Ti coated diamond particles

Sheng Zhang,
Minglu Ding,
Lu Wang,
Wenjun Ge,
Wentao Yan

Affiliations

Sheng Zhang: School of Mechanical Engineering, University of Science and Technology Beijing, PR China; School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, PR China; Corresponding authors at: School of Mechanical Engineering, University of Science and Technology Beijing, PR China (S. Zhang).
Minglu Ding: School of Mechanical Engineering, University of Science and Technology Beijing, PR China
Lu Wang: Department of Mechanical Engineering, National University of Singapore, Singapore 117575, Singapore
Wenjun Ge: Department of Mechanical Engineering, National University of Singapore, Singapore 117575, Singapore; Corresponding authors at: School of Mechanical Engineering, University of Science and Technology Beijing, PR China (S. Zhang).
Wentao Yan: Department of Mechanical Engineering, National University of Singapore, Singapore 117575, Singapore

Journal volume & issue: Vol. 217
p. 110635

Abstract

Read online

Metal matrix composites (MMCs) have received increasing attention and there is a growing interest in additive manufacturing (AM) of MMCs with complex shapes recently. However, it remains challenging to control the quality of composite powder for MMCs. In this study, the diamond particles are firstly coated with thin layers of Titanium and Nickel to ensure strong interface bonding with the Nickel matrix. The influence of ball milling parameters on the Ni-Ti coated diamond/N6 composite powder particles preparation and the effect of processing parameters during laser powder bed fusion (LPBF) on the densification of and defects in the fabricated samples are analyzed. In the ball milling stage, the results show that highly flowable composite powder particles for LPBF can be obtained under a ball milling time of 4 h, a speed of 250 rpm, and a ball-to-powder ratio of 2:1. With the optimized composite powder, a set of Ni-Ti coated diamond/N6 MMCs are further manufactured under the laser powers of 150, 160, and 170 W and scanning speed of 250 mm/s, the MMC samples have relative densities higher than 99%. Our study demonstrates the feasibility of manufacturing dense diamond/N6 and other similar MMCs with appropriate coating, ball-milling and LPBF parameters.

Published in Materials & Design

ISSN: 0264-1275 (Print); 1873-4197 (Online)
Publisher: Elsevier
Country of publisher: United Kingdom
LCC subjects: Technology: Electrical engineering. Electronics. Nuclear engineering: Materials of engineering and construction. Mechanics of materials
Website: https://www.journals.elsevier.com/materials-and-design

About the journal

Abstract

Keywords