Boletín de la Sociedad Española de Cerámica y Vidrio (Apr 2009)
Desarrollo de una nueva mezcla autofraguante para machos de fundición
Abstract
In this paper is described the investigation process and development of a new mixture for foundry cores, in which a factorial complete at two levels experimental design for mixtures with relationships between the components and an operation variable is used. The mixture that is developed uses the traditional process sodium silicate - CO<sub>2</sub> and a new element has been employed: the carbonaceous schist as to facilitate the breaking down of the pieces from de moulds. A nomogram was made, in which it is represented the region where the relationships between components show the best properties, as resistance to the compression and breaking down. Also, it was carried out the integral hygroscopic characterization of the mixture selected as the best, which show excellent hygroscopic properties, compared with the similar ones that use for breaking down the cores, mixtures with sugary compounds.<br><br>En este artículo se describe el proceso de investigación y desarrollo de una nueva mezcla para machos de fundición, en el que se emplea un diseño de experimento para mezclas, factorial completo a dos niveles con relaciones de componentes y variable de operación. La mezcla que se desarrolla utiliza el tradicional proceso silicato de sodio (vidrio líquido) - CO<sub>2</sub> y como elemento novedoso se tiene el empleo de los esquistos carbonosos como aditivo desarenante. Se confecciona un nomograma que presenta la región donde las relaciones entre componentes muestran las mejores propiedades de resistencia a la compresión y desmoldeabilidad para la mezcla en estudio. Además, se realizó la caracterización higroscópica integral de la mezcla seleccionada como de mejores propiedades, la cual mostró excelentes propiedades higroscópicas, comparada con sus similares que emplean desarenantes del tipo azucarado.