Synthesis of La1-xSrxCoO3-δ and its catalytic oxidation of NO and its reaction path

Abstract

The oxidation rate of NO to NO2 is a critical parameter in the removal of NOx within selective catalytic reduction (SCR) systems. LaCoO3-δ is a kind of potential catalyst to enhance the oxidation of NO to NO2, it may offers an economic and stable alternative to noble metal catalysts, particularly at elevated temperatures. This study aimed to enhance the catalytic efficiency of LaCoO3-δ through strontium (Sr) doping. La1-xSrxCoO3-δ (with varying x values of 0.1, 0.2, 0.3, 0.4) was synthesized using a sol-gel method. La1-xSrxCoO3-δ exhibited superior NO oxidation catalytic activity compared to LaCoO3-δ, with the most notable enhancement observed at x = 0.3 (84 % conversion). This improvement can be attributed to the substitution of La3+ with Sr2+, which induces lattice distortion and charge imbalance, thereby creating more oxygen vacancies that enhance the catalytic oxidation capability of La1-xSrxCoO3-δ. However, it's important to note that an excessive amount of Sr can result in the formation of SrCO3 deposits on the surface of La1-xSrxCoO3-δ, thereby diminishing its catalytic oxidation performance. The catalytic oxidation reaction behavior adhered most closely to the O2-adsorbed E-R model, the surface defects in La1-xSrxCoO3-δ playing a pivotal role in the catalytic reaction.

Keywords

• NO oxidation
• Perovskite
• La1-xSrxCoO3-δ
• Catalyst