Fatigue life prediction of gasoline storage tank considering varying current density and weld stress

Abstract

In the field of corrosion fatigue crack research, how to couple corrosion and fatigue under various conditions is a problem worthy of discussion. According to the electrochemical corrosion principles and the superposition principles, studies have been made on the interaction between corrosion and fatigue, and the relationship model between the corrosion fatigue crack size and the corrosion fatigue remaining life in the Corrosion of Hydrogen evolution (COHE) fatigue long crack growth stage is established. The feasibility of the model is verified by using the experimental data. According to the specific structure of the dislocation butt weld of large storage tank, the stress at the crack is calculated. Based on the above model and the experimental data, the corrosion fatigue residual life of large storage tank is predicted. The feasibility of the model is verified, which provides a new method for corrosion fatigue life prediction of large storage tanks.