Durability studies in alkaline activated systems (metakaolin – bottom ash): A prospective study

Abstract

This paper presents an experimental investigation on the durability properties of metakaolin (MK) and bottom ash (BA) blended geopolymer under different environmental exposure. The blended geopolymer concrete (GPC) was prepared with sodium based alkaline activators under ambient curing temperature. The concentration of sodium hydroxide used was 8 M. The ratio of sodium silicate to sodium hydroxide was kept as 2.0. The performance of blended geopolymer concrete was compared with conventional concrete (CC). The test results reveal that blended geopolymer concrete develops a better performance against sulphate and acid resistance. Also, MK-BA GPC shows enhanced performance over the conventional concrete in terms of sorptivity, rapid chloride and water absorption. Resumen: Este artículo presenta una investigación experimental sobre las propiedades de durabilidad del geopolímero mezclado con metacaolín (MK) y cenizas de fondo (BA) bajo diferentes exposiciones ambientales. El hormigón de geopolímero mezclado (GPC) se preparó con activadores alcalinos a base de sodio a temperatura ambiente de curado. La concentración de hidróxido de sodio utilizada fue 8 M. La relación de silicato de sodio a hidróxido de sodio se mantuvo en 2,0. Se comparó el desempeño del concreto geopolímero mezclado con el concreto convencional (CC). Los resultados de las pruebas revelan que el concreto geopolimérico mezclado desarrolla un mejor desempeño frente a la resistencia a los sulfatos y ácidos. Además, MK-BA GPC muestra un rendimiento mejorado sobre el hormigón convencional en términos de sortividad y de rápida absorción de cloruro y agua.

Keywords

• Metacaolín
• Ceniza de fondo
• Curado ambiental
• Durabilidad
• Sortividad
• Absorción de agua