Boletín de la Sociedad Española de Cerámica y Vidrio (Apr 2004)
Influencia del envejecimiento higrotérmico en el comportamiento a fractura de compuestos de matriz termoplástica
Abstract
Aging was carried out by introducing the materials into a climatic chamber under appropriate conditions of temperature, humidity and time. The materials are made of two types of weaving (2/2 Twill, 8H Satin) glass fibre, and (8H Satin) carbon fibre. The matrix was polyetherimide(PEI). In order to characterize the interlaminar fracture a mechanical test was carried out using the mode I Double Cantilever Beam (DCB) and mode II End Notched Fixed (ENF) tests. The analysis consists of knowing the different failure mechanisms which have generated the hygrothermal aging.<br><br>En este trabajo se realiza un estudio sobre la influencia del envejecimiento higrotérmico en el comportamiento a fractura interlaminar de tres tipos de compuestos, dos de ellos reforzados con tejido de fibra de vidrio(2/2 Twill, y 8H Satin) y otro con fibra de carbono (8H Satin) . El envejecimiento se realizó manteniendo, durante diferentes periodos de tiempo, probetas en una cámara climática bajo unas determinadas condiciones de temperatura y humedad relativa. La determinación de la tenacidad a fractura interlaminar se realizó utilizando probetas de modos I (DCB) y II (ENF). El análisis realizado consistió en poner de manifiesto los diferentes mecanismos de rotura a fractura que se generan tras someter las probetas a la exposición higrotérmica. De los resultados de los ensayos se concluye un diferente comportamiento a fractura según el refuerzo existente y también a igual refuerzo, según la trama del tejido.