Roughness and stability of compound resin color exposed to bleaching strips after surface treatment

Abstract

ABSTRACT Objective to analyze the surface roughness and color stability of the composite resin after surface treatment with the aluminum oxide discs and subsequent exposure to the Advanced Teeth Whitening Strips. Methods 20 specimens of the Filtek Z350XT restorer (3M®) were prepared and daily subjected to home bleaching for 30 minutes during 14 days. A precision rugosimeter was used in order to verify the roughness by means of 3 random readings in the same direction in each sample. For color stability the CIELAB system (L*, a*, b* values) was used through the spectrophotometer (MINOLTA CR -321, Japan). The means of the test specimens as well as the mean of each group were calculated using the random readings. Data statistical analysis were performed by ANOVA- analysis of variance. The level of significance was set at 5% (p ≤ 0.05). Results Roughness did not present great numerical variations. No statistically significant difference between the means obtained concerning the surface roughness of the composite resin with p = 0.44 was observed. However, it was found that there was a statistically significant difference between the means obtained in relation to the color stability of the composite resin, p=0. 007. Conclusion It was concluded that pre-contoured strips containing 6% hydrogen peroxide do not have a significant adverse effect on the roughness of Z350XT (3M®) resin. However, it was also concluded that according to the color stability analysis performed, there may be an indication of the restoration replacement after the bleaching treatment, due to their color change.

Keywords

• Composite resins
• Tooth bleaching
• Dental polishing