Boletín de la Sociedad Española de Cerámica y Vidrio (Aug 2004)
Preparación y caracterización de óxidos de cobalto Cuasi-bidimensionales Ln<sub>1-x</sub>Sr<sub>1+x</sub>CoO<sub>4</sub> (Ln= La, Nd y Gd)
Abstract
By using the nitrate decomposition method in the presence of KNO3, we have been able to enlarge the compositional range of the cobaltlayered compounds Ln1-xSr1+xCoO4 (Ln: La, Nd, Gd) to 0≤x≤0.40 in the case of lanthanum, to 0≤x≤0.30 for neodymium, and to 0≤x≤0.20 in the case of gadolinium. In this work we present the results of their structural characterization by means of powder X-ray diffraction (PXD) and Rietveld analysis as a function of composition (x) and the rare earth (Ln), information that has been complemented by infrared spectroscopy (IR), electron diffraction (ED) and electron microscopy.Mediante el método de descomposición de nitratos en presencia de KNO3, se ha conseguido aumentar el rango composicional de los compuestos cuasi-bidimensionales de cobalto Ln1-xSr1+xCoO4 (Ln: La, Nd y Gd), a 0≤x≤0.4 cuando Ln = La, 0≤x≤0.3 cuando Ln = Nd y 0≤x≤0.2 cuando Ln = Gd. En este trabajo se presentan los resultados de su caracterización estructural mediante difracción de rayos X en polvo (DRX) y análisis Rietveld tanto en función de la composición (x) como de la tierra rara (Ln), información que se complementa con datos de espectroscopía de infrarrojo (IR), difracción de electrones (DE) y microscopía electrónica (ME).