An investigation on anti-impact and penetration performance of basalt fiber composites with different weave and lay-up modes

Abstract

The woven basalt fiber composites (WBFC) and the unidirectional [0°/90°/45°/-45°]s basalt fiber composites (UBFC) were prepared by hot-pressing. Three-point bending test, low velocity impact test, and ballistic test were performed to the prepared composites. After the tests, the specimens were recovered and analyzed for micromorphology. Three-point bending tests show that both the bending strength and stiffness of the WBFC surpass those of the UBFC. Low velocity impact test results show that the low velocity impact resistance to hemispherical impactor of the UBFC is higher than that of the WBFC, but the low velocity impact resistance to sharp impactor of the UBFC is lower than that of the WBFC. For the ballistic test, it can be found that the ballistic property of the UBFC is higher than that of the WBFC. After the tests, microscopic analysis of the specimens was applied, and their failure mechanism was discussed. The main failure modes of the UBFC are delamination and fibers breakage under the above loading conditions while the main failure mode of the WBFC is fibers breakage. Although delamination damage can be found in the WBFC under the above loading conditions, the degree of delamination is far less than that of the UBFC.

Keywords

• The woven basalt fiber composites
• The [0°/90°/45°/-45°]s basalt fiber composites
• Low velocity impact
• Ballistic test
• Delamination