Boletín de la Sociedad Española de Cerámica y Vidrio (Apr 2004)
Influencia de la adición de galio en las propiedades estructurales y texturales de óxidos de Mn y Al
Abstract
Mn-Ga and Al-Ga mixed oxides have been prepared in all compositional range by a conventional co precipitation method and subsequent thermal treatments. In the Al-Ga mixed oxide system, solid solutions are observed for samples up to 50% Ga content, identifying only the γ-Al2O3 phase below 800 ºC and the α-Al2O3 phase for temperatures above 800 ºC. BET specific surface decreases significantly as Ga addition increases. Ga-addition to manganese oxide produce phases no thermodynamically stable, but very interesting from the catalytic point of view, i.e. MnO2 in samples with 10% Ga content and treated at 400 ºC. Increasing the temperature, biphasic materials composed by Mn3O4 (hausmannita) y Mn2O3 (bixbyita) phases are identified in the X-ray patterns for Ga contents > 20%. These data are complemented by the evolution of FT-IR and electronic spectra.<br><br>Se han obtenido óxidos mixtos de los sistemas Mn-Ga y Al-Ga en todo el intervalo de composiciones mediante un método de coprecipitación convencional y posteriores tratamientos térmicos. En el sistema Al-Ga, se observan soluciones sólidas hasta el 50% de Ga3+ identificándose la fase γ-Al2O3 por debajo de 800 ºC y la fase α-Al2O3 para temperaturas superiores. Las superficies específicas BET disminuyen con el incremento del contenido de Ga. La adición de Ga (10% en moles y 400 ºC) al óxido de manganeso origina la obtención de fases termodinámicamente inestables, como el MnO2 (pirolusita), interesantes desde el punto de vista catalítico. El aumento de temperatura conduce a mezclas de fases Mn3O4 (hausmannita) y Mn2O3 (bixbyita) para contenidos de Ga mayores del 20%. Estos datos se complementan por las variaciones observadas en los espectros FT-IR y electrónicos.