Hemijska Industrija (Jan 2013)
Effect of tungsten carbide in carbon Pt catalyst support on electrochemical oxygen reduction in acid solution
Abstract
Tungsten carbide was synthesized by calcination of carbon cryogel with embedded tungsten in a form of metatungstate. This material was used as a support for Pt nanoparticles. XRD pattern of W-C support indicates the presence of WC, W2C, and unreacted W, as well as graphitized carbon. According to the previous TEM analysis of W-C support, it contains particles with core-shell structure, where W particle was covered with the shell of a mixture of WC and W2C. The average Pt grain size calculated from XRD pattern was about 6 nm. Cyclic voltammogram of W-C support was recorded within potential range relevant for its application as a catalyst support in fuel cells. Pair of anodic/cathodic peaks close to the negative potential limit could be ascribed to the intercalation of hydrogen within hydrous tungsten oxide, which is always present on the surface of WC in aqueous solutions. Cyclic voltammogram of Pt/W-C indicated that tungsten oxide species are present on tungsten carbide shell as well as on the surface of Pt nanoparticles. Pt surface is only partially covered by hydrous tungsten oxide. Hydrogen intercalation in hydrous tungsten oxide is enhanced in the presence of Pt nanoparticles. Also, the presence of hydrated tungsten oxide leads to the decrease of OH chemisorbed on Pt surface. Stripping of underpotentially deposited copper was used for the assessment of Pt surface area and the specific surface area of Pt was estimated to 41 m2 g-1. Electrochemical oxygen reduction reaction was examined on the synthesized Pt/W-C catalyst and compared with the results on the commercial Pt/C catalyst. It was found that the current densities at Pt/W-C are almost double as those on Pt/C. The Tafel plots for both catalysts are characterized with two Tafel slopes: -0.060 V dec-1 at low current densities, and -0.120 V dec-1 at high current densities. From the rotational dependence of the reaction rate, it was found that oxygen reduction on both Pt/W-C and Pt/C follows the first order kinetics with respect to O2 and that four electrons are transferred per O2 molecule. The results show that the presence of tungsten carbide in support material i.e. hydrous tungsten oxide on Pt surface, leads to promotion of oxygen reduction on the Pt/W-C catalyst. It was assumed that oxophilic hydrated tungsten oxide hinders OH adsorption on Pt surface, thus increasing Pt surface area available for O2 adsorption and its electrochemical reduction.
Keywords