Effects of temperature and concentration of La in the form of A1 transverse optical phonon in the PbTiO3 system Efeitos da temperatura e concentração de La na forma de fótons ópticos transversais A1 no sistema PbTiO3

Abstract

The structural phase transition from ferroelectric to paraelectric was studied by Raman scattering in the ceramic lead titanate (PbTiO3) doped with lanthanum (La). A1 vibrational mode contains some sub-peaks that have been associated in literature with PbTiO3 concentration (Ca, Ba), and effects of high temperatures as it approaches the Curie temperature (Tc). Raman new study shows that the anomalous behavior of the A1 mode is not only caused by the effects of concentration or temperature near Tc, but by anharmonicity and defects in the network in the PbTiO3 thermodynamically are inevitable. This effect was studied by a wide temperature range from 10 K to Tc in each sample (La = 0, 5, 10, 15, 20%), showing that the effect depends not only on the high temperatures in the pure PT.A transição de fase estrutural de ferroelétrico para paraelétrico foi estudada por espalhamento Raman em cerâmicas de titanato de chumbo (PbTiO3) dopadas com lantânio (La). O modo vibracional A1 contém alguns picos que tem sido associados na literatura com a concentração de PbTiO3 (Ca, Ba), e os efeitos das altas temperaturas ao se aproximar da temperatura de Curie (Tc). Um novo estudo Raman mostra que o comportamento anômalo do modo A1 não é apenas causado pelos efeitos da concentração ou da temperatura próxima de Tc, mas por anarmonicidade e defeitos na rede do PbTiO3 são termodinamicamente inevitáveis. Este efeito foi estudado em uma ampla faixa de temperatura de 10 K a Tc em cada amostra (La = 0, 5, 10, 15, 20%), mostrando que o efeito depende não somente das altas temperaturas no PT puro.

Keywords

• PbTiO3
• ferroelétrico
• paraelétrico
• anarmonicidade
• PbTiO3
• ferroelectric
• paraelectric
• anharmonicity