Defect- and H-Free Stoichiometric Silicon Carbide by Thermal CVD from the Single Source Precursor Trisilacyclohexane

Abstract

Stoichiometric silicon carbide (SiC) thin films were grown using thermal chemical vapor deposition (TCVD) from the single source precursor 1,3,5-trisilacyclohexane (TSCH) on c-Si (100) substrates within an optimized substrate temperature window ranging from 650 to 850 °C. X-ray photoelectron spectroscopy (XPS) and Fourier transform infrared spectroscopy (FTIR) analyses revealed that the as-deposited films consisted of a Si-C matrix with a Si:C ratio of ~1:1. FTIR and photoluminescence (PL) spectrometry studies showed that films deposited ≥ 750 °C were defect- and H-free within the detection limit of the techniques used, while ellipsometry measurements yielded an as-grown SiC average refractive index of ~2.7, consistent with the reference value for the 3C-SiC phase. The exceptional quality of the films appears sufficient to overcome limitations associated with structural defects ranging from failure in high voltage, high temperature electronics to 2-D film growth. TSCH, a liquid at room temperature with good structural stability during transport and handling as well as high vapor pressure (~10 torr at 25 °C), provides a viable single source precursor for the growth of stoichiometric SiC without the need for post-deposition thermal treatment.

Keywords

• silicon carbide
• SiC
• chemical vapor deposition
• CVD
• thin film
• organosilicon