Effect of Nano-Si₃N₄ Reinforcement on the Microstructure and Mechanical Properties of Laser-Powder-Bed-Fusioned AlSi10Mg Composites

Abstract

Laser powder bed fusion (LPBF) technology is of great significance to the rapid manufacturing of high-performance metal parts. To improve the mechanical behavior of an LPBFed AlSi10Mg alloy, the influence of nano-Si3N4 reinforcement on densification behavior, microstructure, and tensile property of AlSi10Mg was studied. The experimental results show that 97% relative density of the 3 vol.% nano-Si3N4/AlSi10Mg composite was achieved via optimization of the LPBF process. With the increase in the nano-Si3N4 content, the tensile strength and the yield strength of the composite steadily increase as per the Orowan strengthening mechanism while the elongation decreases. In addition, nano-Si3N4 reinforcement reduces the width of the coarse cell structure region and the thermal influence region of the AlSi10Mg matrix. After annealing, the tensile strength of the nano-Si3N4/AlSi10Mg composite decreases and the elongation increases significantly.

Keywords

• laser powder bed fusion (LPBF)
• nano-Si₃N₄
• AlSi10Mg
• mechanical properties
• heat treatment