Revisiting the condensation reaction of lignin in alkaline pulping with quantitativity part I: the simplest condensation between vanillyl alcohol and creosol under soda cooking conditions

Abstract

Abstract The condensation reaction of lignin is believed to interfere with delignification in alkaline pulping processes, without any clear evidence, which has motivated us to quantitatively revisit it. This paper is the first of a series, and hence we employed the simplest model system using 4-hydroxymethyl-2-methoxyphenol (vanillyl alcohol, Va) and 2-methoxy-4-methylphenol (creosol, Cr) under soda cooking conditions. The α-5-type condensation product between these compounds [VaCr, 2-(4-hydroxy-3-methoxybenzyl)-6-methoxy-4-methylphenol] was identified and quantified as exclusive. VaCr was yielded with a mole amount of 24%, 46%, 62%, or 72% based on that of disappearing Va at a reaction time of 120 min when the ratio of the initial concentration of Cr to that of Va was 1.0, 2.5, 5.0, or 7.5, respectively. These yields and an HPLC analysis of the reaction solution obtained by a treatment of Va as the sole compound under the same soda cooking conditions suggested the formation of self-condensation products of Va even in the treatments containing Cr. The obtained results comprehensively suggested that the self-condensation of Va progresses more readily than the condensation between Va and Cr. The factors behind this will be the topic of our next paper.

Keywords

• Alkaline pulping
• Condensed structure
• Delignification
• Quinone methide