Materials (Jun 2024)
Synthesis of Low-Silicon X-Type Zeolite from Lithium Slag and Its Fast Exchange Performance of Calcium and Magnesium Ions
Abstract
Without the addition of silicon and aluminum sources, a pure-phase KNaLSX zeolite was successfully synthesized from the residue (lithium slag), which was produced from spodumene in the production process of lithium carbonate. The KNaLSX samples were characterized by an X-ray Diffractometer (XRD), Scanning Electron Microscope (SEM), X-ray Fluorescence Spectrometer (XRF), Thermogravimetric Differential Thermal Analysis (TG-DTA), Fourier Transform Infrared Spectrometer (FT-IR), and N2 adsorption measurement. The ion exchange capacity and the ion exchange rate of calcium and magnesium ions were measured as used for a detergent builder, and the results were compared with the standard zeolites (KNaLSX and 4A). The experimental results show that the pure-phase KNaLSX synthSynthesis and characterization of co-crystalline zeolite composite of LSX/esized from lithium slag has a SiO2/Al2O3 ratio of 2.01 with a grain size of 3~4 μm, which is close to the commercial KNaLSX sample of a SiO2/Al2O3 ratio of 2.0. The BET-specific surface area of KNaLSX is 715 m2/g, which is larger than the low-silicon X-type zeolite (LSX) synthesized from waste residue reported in the literature. The ion exchange rate constant of calcium and magnesium ions in KNaLSX is 5 times and 3 times that of 4A zeolite, respectively. KNaLSX also has a high ion exchange capacity for magnesium ion of 191 mgMgCO3/g, which is 2 times than that of 4A zeolite, and a high ion exchange capacity for calcium ion of 302 mgCaCO3/g, which meets the first-grade standard of zeolite for detergent builders in China. The work provides the basis for high-value resource utilization of lithium slag and the development of a detergent builder for rapid washing.
Keywords