Different Roles of Ce³⁺ Optical Centers in Oxyorthosilicate Nanocrystals at X-ray and UV Excitation

Abstract

Luminescence properties of Lu2SiO5:Ce3+ and Y2SiO5:Ce3+ nanocrystals were studied using photo- and X-ray luminescence techniques. The crystal structure of Re2SiO5 nanocrystals (P21/c space group) differs from the crystal structure of Re2SiO5 bulk crystals (C2/c space group) with 9- and 7-oxygen-coordinated cation positions instead of 6- and 7-coordinated ones observed for Re2SiO5 bulk crystals. Two optical centers (Ce1 and Ce2) were observed for Re2SiO5:Ce3+ nanocrystals originating from cerium ions substituting 9- and 7-oxygen-coordinated cation sites. Preferential substitution of larger cation sites by cerium ions leads to higher photoluminescence intensity of Ce1 centers, however, Ce2 centers are the main centers for electron-hole recombination, so only Ce2 band is observed in X-ray luminescence spectra. The features of oxygen coordination of Ce1 and Ce2 centers and high content of oxygen vacancies in Re2SiO5:Ce3+ nanocrystals can provide preferential trapping of electrons near Ce2 centers, and therefore, the dominant role of Ce2 band in X-ray luminescence spectra.

Keywords

• cerium
• luminescence
• lutetium silicate
• yttrium silicate
• nanocrystals